SWD961 Series SH138 room temperature cure water

    base system ship cabin internal environment friendly

special iron oxide red anticorrosion primer

Descriptions               Ship painting operation goes through the whole process of ship construction. when usually applies with welding construction, the most commonly anticorrosion coating which is oil base, so large amounts of solvent will be volatized then cause to fires accidents in slightest negligence. After years of scientific research, SWD Urethane Co., USA developed water base ship internal cabine special iron oxide red anticorrosion protective primer. It is a new environment friendly green coating product can be safely painted in the case of normal ship construction.

Characteristics           Through special precision formulation and scientific process this primer takes environment friendly water base high molecule polymer resin and high-quality iron oxide red as main raw material. the primer is dense, with good plugging performance and penetrate resistance and excellent performance of salt water resistance, wet resistance, oil resistance, rust resistance and anticorrosion. High adhesive strength on the metal substrate, good bond strength with the following coating, the water base primer is easy to use, without pollution in and after application.

Specifications

Adhesive strength (grid method)                 class 1

Impact resistance                             ≥50kg•cm

Temperature variation                         -40------+150℃

Wear resistance（700g/500r）                  13mg

Acid resistance 30%H₂SO₄ or 10%HCI, 30d        no rust no bubbles no peel

Alkali resistance 30%NaOH, 30d                 no rust no bubbles no peel

Salt resistance 80g/L, 30d                       no rust no bubbles no peel

Salt spray resistance 1000h                      no rust no bubbles no peel

Oil resistance 0# diesel Crude oil 30d              no rust no bubbles no peel  

Data of performance

Color                        Multiple colors as customers’ need

Luster                        glazed

Density                       1.27g/cm³

Volume solid content            63%±2%

VOC                         ≤78g/L

Recommended dry film thickness   30-80μm

Theoretical coverage             0.12kg/sqm (calculated by the above solids percentage and dry film thickness of 50 microns)

Practical coverage                Allow appropriate loss rate

Dry time                       1-3h

Overcoating interval              min: 3h, max: 28h

Overcoating method              Airless spray, Air spray, Brush, Roller

Flash point                  Non flammable, non explosive, safety and environmental protection

Recommend procedures

Application scope          Ship internal cabin anticorrosion painting

Shelf life         12 months (Indoor with dry and cool conditions, frozen below 0℃)

Packing                    20kg/bucket. 25kg/bucket

Production area            Minhang district, City of Shanghai（25% of raw materials  imported from SWD US）

Security                   To apply this product must be accordance with the relevant national regulation of sanitation, safety and environment. Avoid contacting the wet coating.

Global applicability         Our company aims to provide worldwide customers the same coatings, but sometimes, some small adjustments are made to satisfy each region conditions and international norms, in this case, an alternative product data will be provided.

 Integrity declaration         Our company guarantees the reality of the listed data, due to the diversity and variability of the application environment, please test and verify it before use. We don’t take any other responsibilities except the coating quality self and reserve the right of modification the listed data without prior notice.